Shot Blasting Ductile Cast Iron parts 65-45-12 60-40-18 Material

Categories Ductile Cast Iron
Brand Name: non-standard
Model Number: custom-built
Certification: ISO9001;TS16949
Place of Origin: China
MOQ: 1 Ton
Price: quote according to drawing technical requirements
Payment Terms: T/T, L/C
Supply Ability: 300 Tons every month
Delivery Time: within 60 days
Packaging Details: Plywood crate + VCI Anti-Rust Bag
Name: Ductile Cast Iron Parts
Material: 65-45-12 60-40-18 Material
Process: Moulding Machine Green Sand Casting
Machining: CNC Machining
Surface: Shot Blasting
Packing: Crate
  • Product Details
  • Company Profile

Shot Blasting Ductile Cast Iron parts 65-45-12 60-40-18 Material

Shot Blasting Ductile Cast Iron Parts 65-45-12 60-40-18 Material


Product Material and Uses


1. Normally produce with gray iron HT200, HT250, ductile iron 65-45-12, 60-40-18, 80-55-06, 80-60-03, etc.

2. The ductile iron casting products are widely used for Auto-cars, trains, trucks, vehicle components, mining machinery components, agricultural machinery parts, textile machinery parts, construction machinery parts, valves and pump parts, etc.


What is in Ductile Iron? (Composition)

If you were to do a chemical analysis of ductile iron, this is what you would normally find:

Iron ~94%

Carbon 3.2 – 3.60%

Silicon 2.2 – 2.8%

Manganese 0.1 – 0.2%

Magnesium 0.03 – 0.04%

Phosphorus 0.005 – 0.04%

Sulfur 0.005 – 0.02%

Copper <= 0.40%


Common Ductile Iron Grades


While there are many different ductile iron specifications, foundries routinely offer 3 common grades;


Physical and Mechanical PropertiesASTM A536, Grade 60-40-18ASTM A536, Grade 65-45-12ASTM A536, Grade 80-55-06
Tensile Strength, min, psi60,00065,00080,000
Tensile Strength, min, MPa414448552
Yield Strength, min, psi40,00045,00055,000
Yield Strength, min, MPa276310379
Elongation in 2 in. or 50 mm, min %18126
Density lb/in30.2560.2560.256
Density g/cm37.17.17.1
Melting Temperature (Degrees F)2,100 – 2,1902,100 – 2,1902,100 – 2,190
Melting Temperature (Degrees C)1,150 - 1,2001,150 - 1,2001,150 - 1,200
Compressive Strength Ksi429429429
Compressive Strength MPa296029602960
UNSF32800F33100F33800

Grade 80-55-06 (187 – 255 BHN)


80-55-06 contains approximately 50% ferrite / 50% pearlite, although the composition can vary depending on the producer. This grade is slightly less machinable than 65-45- 12 and is used when better wear resistance and higher strengths are required. It is a good replacement for medium carbon steels including: 1040, 1060, 1045, 1141, 1144.


Cheap Shot Blasting Ductile Cast Iron parts 65-45-12 60-40-18 Material for sale
Send your message to this supplier
 
*From:
*To: Zhengzhou Yu-Long Machinery Equipment Co., Ltd.
*Subject:
*Message:
Characters Remaining: (0/3000)
 
You may also be interested in :
Inquiry Cart 0
  • Haven't found right suppliers
  • Our buyer assistants can help you find the most suitable, 100% reliable suppliers from China.
  • And this service is free of charge.
  • we have buyer assistants who speak English, French, Spanish......and we are ready to help you anytime!
  • Submit Buying Request
    Contact Us Quickly