Ductile Cast Iron 60-40-18 Material Precision Casting Auto Spare Parts Tractor Parts

Categories Ductile Cast Iron
Brand Name: non-standard
Model Number: custom-built
Certification: ISO9001;TS16949
Place of Origin: China
MOQ: 1 Ton
Price: quote according to different drawing technique requirements
Payment Terms: T/T, L/C
Supply Ability: 300 Tons every month
Delivery Time: within 60 days
Packaging Details: Plywood crate + VCI Anti-Rust Bag
Material: Ductile iron GGG40
Process: Precoated Sand Casting Process
Machining: CNC Machining
Surface: Anti-Rust Oil
Used for: Autocar Industry
Packing: Crate
  • Product Details
  • Company Profile

Ductile Cast Iron 60-40-18 Material Precision Casting Auto Spare Parts Tractor Parts

Product Description and Process


1.Ductile Cast Iron 60-40-18 Material Precision Casting Auto Spare Parts Tractor Parts


2. Production process: green sand molding, pre-coated sand molding and resin sand molding which can produce iron castings from 50 gram to 2000 kilograms


3. Machining process: CNC machine, machining center, lathe, mill machine, drill machine, etc.


4. Surface treatment process: paint coating, electrophoretic coating, electrogalvanizing coating, black oxide coating, phosphate coating, powder coating, etc.


Product Material and Uses


1. Normally produce with gray iron HT200, HT250, Ductile Iron 65-45-12, 60-40-18, 80-55-06, 80-60-03, etc.

2. The ductile iron casting products are widely used for Auto-cars, trains, trucks, vehicle components, mining machinery components, agricultural machinery parts, textile machinery parts, construction machinery parts, valves and pump parts, etc.


Ductile Iron Castings & Ductile Cast Iron


If cast iron is subject to a compressive load, these stress points are not particularly detrimental and flake graphite cast iron is excellent under compression. However, tensile loading above the natural tensile strength of the cast iron can cause rapid tensile failure as cracks propagate rapidly out from these stress points. The result of this is that cast iron has virtually no elongation, is a brittle material and is therefore limited in its use in tensile and shock loading applications. For years foundrymen and metallurgists tried to develop a new type of cast iron that would withstand bending and shock loading and would have the characteristics more of malleable cast iron but could be produced at the lower cost of grey cast iron. This resulted in the development of Ductile Cast Iron.



China Ductile Iron Auto Parts

The main products includes small wheel hub, reducer shell, differential shell, ductile iron brackets, idle wheels, and flywheels.


The material grades ductile iron ASTM A536 60-40-18, 65-45-12, 70-50-05, 80-55-06, 80-60-03, 100-70-03.



  1. Materials:
    Ductile Iron, SG Iron, Nodular Iron

  2. Material Grades:
    ASTM A536 60-40-18, 65-45-12, 70-50-05, 80-55-06, 80-60-03, 100-70-03; DIN 1693 GGG40, GGG50, GGG60, GGG70.

  3. Equal Standards:
    ISO 1083, GB 1348, DIN 1693, EN 1563, JIS G5502, UNI 4544, NF A32-201, BS 2789, IS 1865, UNF, NBN 830-02, AS 1831, SS 14 07, NS11 301

  4. Application:
    Automotive, Vehicle, Car, Truck, Mining Machinery, Tractor

  5. Production Process:
    Automatic Molding Line, Green Sand, Shell Molding

  6. Exported to: USA, Italy, Germany, France, Australia

What is in Ductile Iron? (Composition)

If you were to do a chemical analysis of ductile iron, this is what you would normally find:

Iron ~94%

Carbon 3.2 – 3.60%

Silicon 2.2 – 2.8%

Manganese 0.1 – 0.2%

Magnesium 0.03 – 0.04%

Phosphorus 0.005 – 0.04%

Sulfur 0.005 – 0.02%

Copper <= 0.40%

To improve the strength of ductile iron, additional tin or copper can be added. To improve corrosion resistance, copper, nickel, or chromium can replace anywhere from 15-30% of the iron.


Common Ductile Iron Grades


While there are many different ductile iron specifications, foundries routinely offer 3 common grades;


Physical and Mechanical PropertiesASTM A536, Grade 60-40-18ASTM A536, Grade 65-45-12ASTM A536, Grade 80-55-06
Tensile Strength, min, psi60,00065,00080,000
Tensile Strength, min, MPa414448552
Yield Strength, min, psi40,00045,00055,000
Yield Strength, min, MPa276310379
Elongation in 2 in. or 50 mm, min %18126
Density lb/in30.2560.2560.256
Density g/cm37.17.17.1
Melting Temperature (Degrees F)2,100 – 2,1902,100 – 2,1902,100 – 2,190
Melting Temperature (Degrees C)1,150 - 1,2001,150 - 1,2001,150 - 1,200
Compressive Strength Ksi429429429
Compressive Strength MPa296029602960
UNSF32800F33100F33800

GB/T 1348 1998 (China)


Grade

Tensile strength

σb≥/MPa

Yield strength

σ0.2≥/MPa

Elongation

δ5≥(%)

Hardness

HBS

QT400-18

QT400-18-LT*

40025018130~180
QT400-1540025015130~180
QT450-1045031010160~210
QT500-75003207170~230
QT600-36003703190~270
QT700-27004202225~305
QT800-28004802245~335
QT900-29006002280~360

Product Tags:

nodular cast iron

  

spheroidal cast iron

  
Cheap Ductile Cast Iron 60-40-18 Material Precision Casting Auto Spare Parts Tractor Parts for sale
Send your message to this supplier
 
*From:
*To: Zhengzhou Yu-Long Machinery Equipment Co., Ltd.
*Subject:
*Message:
Characters Remaining: (0/3000)
 
You may also be interested in :
Inquiry Cart 0
  • Haven't found right suppliers
  • Our buyer assistants can help you find the most suitable, 100% reliable suppliers from China.
  • And this service is free of charge.
  • we have buyer assistants who speak English, French, Spanish......and we are ready to help you anytime!
  • Submit Buying Request
    Contact Us Quickly