Water Pump Impeller Parts Graphite Cast Iron GGG-40 Material ASTM A536

Categories Ductile Cast Iron
Brand Name: non-standard
Model Number: custom-built
Certification: ISO9001;TS16949
Place of Origin: China
MOQ: 1 Ton
Price: quote according to different drawing technique requirements
Payment Terms: T/T, L/C
Supply Ability: 300 Tons every month
Delivery Time: within 60 days
Packaging Details: Plywood crate + VCI Anti-Rust Bag
Material: GGG40
Process: Green Sand Casting Process
Machining: CNC Machining
Surface: Anti-Rust Oil
Used for: Pump Industry
Packing: Crate
  • Product Details
  • Company Profile

Water Pump Impeller Parts Graphite Cast Iron GGG-40 Material ASTM A536

Water Pump Impeller Parts Graphite Cast Iron GGG-40 Material ASTM A536


Product Description and Process

1.Water Pump Impeller Parts Ductile iron Castings GGG-40 Material Sand Casting Foundry

2. Production process: green sand molding, pre-coated sand molding and resin sand molding which can produce iron castings from 50 gram to 2000 kilograms

3. Machining process: CNC machine, machining center, lathe, mill machine, drill machine, etc.

4. Surface treatment process: paint coating, electrophoretic coating, electrogalvanizing coating, black oxide coating, phosphate coating, powder coating, etc.

Product Material and Uses
1. Normally produce with gray iron HT200, HT250, ductile iron 65-45-12, 60-40-18, 80-55-06, 80-60-03, etc.
2. The ductile iron casting products are widely used for Auto-cars, trains, trucks, vehicle components, mining machinery components, agricultural machinery parts, textile machinery parts, construction machinery parts, valves and pump parts, etc.


What is Ductile Iron Used For? (Applications)

Ductile iron is great for use where you need strong metal with wear resistance.
Here is a sample list of things made from or contain ductile iron:
Pipe and pipe fittings (almost 50% of ductile iron sold in the US is for pipe and fittings)
Axles
Connecting rods (like in engines)
Crankshafts
Cylinders
Disc brake calipers
Gears and Gear Boxes
Housings and manifolds
Hydrostatic Barrels
Idler arms
Large Machines
Machine Tooling
Military uses
Piano Harps (the part that holds the strings of a piano)
Spindle supports
Steering knuckles
Suspension system parts
Truck axles
Valves (especially high-pressure valves)
Wheel hubs
Yokes for power transmission





What is the difference between Ductile Iron and Cast Iron?
Cast iron refers to all iron parts that are cast and have a high carbon content, but in normal usage, “cast iron” refers to gray iron, the cast parts with weaker iron structures containing graphite flakes. Ductile iron must specifically have the spherical graphite structure in the metal.
Regular cast iron can be cast cheaply, machined very easily, and strength can be added through heat treating. Gray iron lacks the strength and durability of ductile cast iron. Ductile iron castings are not much more expensive than gray iron castings yet if there is no need for the benefits of ductile iron you should probably stick with the gray iron castings.

What is in Ductile Iron? (Composition)

If you were to do a chemical analysis of ductile iron, this is what you would normally find:
Iron ~94%
Carbon 3.2 – 3.60%
Silicon 2.2 – 2.8%
Manganese 0.1 – 0.2%
Magnesium 0.03 – 0.04%
Phosphorus 0.005 – 0.04%
Sulfur 0.005 – 0.02%
Copper <= 0.40%
To improve the strength of ductile iron, additional tin or copper can be added. To improve corrosion resistance, copper, nickel, or chromium can replace anywhere from 15-30% of the iron.

Ductile Iron Grade Chart
ASTM A536 1993 (USA)

GradeTensile Strength
σ≥/Mpa
Yield Strength
σ≥/Mpa
Elongation
δ≥(%)
ANSI/ASTMUNS
60-40-18F3280041427618
65-45-12F3310044831012
80-55-06F338005523796.0
100-70-03F348006894833.0
120-90-02F362008276212.0
Special Purpose
60-42-1041529010
70-50-054853455.0
80-60-035554153.0



Common Ductile Iron Grades

While there are many different ductile iron specifications, foundries routinely offer 3 common grades;

Physical and Mechanical PropertiesASTM A536, Grade 60-40-18ASTM A536, Grade 65-45-12ASTM A536, Grade 80-55-06
Tensile Strength, min, psi60,00065,00080,000
Tensile Strength, min, MPa414448552
Yield Strength, min, psi40,00045,00055,000
Yield Strength, min, MPa276310379
Elongation in 2 in. or 50 mm, min %18126
Density lb/in30.2560.2560.256
Density g/cm37.17.17.1
Melting Temperature (Degrees F)2,100 – 2,1902,100 – 2,1902,100 – 2,190
Melting Temperature (Degrees C)1,150 - 1,2001,150 - 1,2001,150 - 1,200
Compressive Strength Ksi429429429
Compressive Strength MPa296029602960
UNSF32800F33100F33800

Product Tags:

nodular cast iron

  

graphite cast iron

  
Cheap Water Pump Impeller Parts Graphite Cast Iron GGG-40 Material ASTM A536 for sale
Send your message to this supplier
 
*From:
*To: Zhengzhou Yu-Long Machinery Equipment Co., Ltd.
*Subject:
*Message:
Characters Remaining: (0/3000)
 
You may also be interested in :
Inquiry Cart 0
  • Haven't found right suppliers
  • Our buyer assistants can help you find the most suitable, 100% reliable suppliers from China.
  • And this service is free of charge.
  • we have buyer assistants who speak English, French, Spanish......and we are ready to help you anytime!
  • Submit Buying Request
    Contact Us Quickly